摘　要：以我国杉木等木材为试验材料，采用自制小型热处理木材试验装置进行了蒸汽法木材热处理工艺试验。结果表明：在热处理初期，待处理木材的含水率应小于15%，迅速升温至100℃，再缓慢升温到130℃干燥到绝干，再迅速升温到热处理目标温度，一般应控制在180℃-220℃范围内，处理时间根据需要确定，一般为2-4h；在处理过程中应适当喷蒸，降到80℃，调整含水率到4%-8%，出窑。上述工艺切实可行。

关键词：蒸汽　木材　热处理　工艺

Abstract: This article use the Chinese fir and other wood as the experimental materials. The elementary research of the thermowood process are studied using heat-treated equipments made by self. It is concluded that:the moisture content of wood should be below 15%,wood should be dryed absolutely at 130℃.The target temperature should be from 180℃ to 220℃,on the average ,the time should be controlled between 2 hour and 4 hours.In the course of treating,the steam should be spurted properly.When the temperature falls down,the moisture content is controlled 4%-8%.The process is feasible.

Key words: Stream, Wood, Heat-treated, Process

　　随着国家天然林保护工程的实施，人工林木材的开发利用已成为解决木材供需矛盾的重要途径。蒸汽法木材热处理工艺的研究，是高效利用木材，提高木材附加值的物理加工手段。热处理木材既具有良好的尺寸稳定性、耐腐性、耐候性、环保性等优点，又可通过热处理改变普通木材的颜色来模仿珍贵木材，提高其使用范围和附加值，已越来越受到企业和木材科学研究人员的关注。

　　自从上个世纪中叶，不同的木材热处理改性工艺在法国、芬兰、荷兰和德国就发展起来并产业化^[1]，而国内关于木材热处理工艺的研究甚少。因此，借鉴国外木材热处理方法和经验，适时开展我国木材热处理改性研究尤为重要。

1 试验材料与方法

1.1 试验材料

　　试验所用的人工林杉木木材，采自浙江省临安市马溪木材市场，试验材规格：22mm×150 mm×350mm（厚度×宽度×长度），含水率为16%-30%。材料要求：挑选时要尽量注意选少节或无死节的试件，试件以径向板为佳。

1.2 设备

　　MWD-50微机控制电子式木材万能试验机、101-1型电热鼓风干燥箱、日本ESPEC调温调湿箱、自制小型木材热处理装置。

　　自制小型木材热处理装置（原理图，见图1）由以下组成部分：（1）蒸汽发生器，主要提供热处理过程中所需蒸汽；（2）电热恒温烘箱，堆放木料和提供热源；（3）温度显示仪，主要测定木材表、心层的温度，从而实现连续检测，便于控制升温速度；（4）轴流式风机,主要实现装置内介质快速循环；（5）隔板，防止木材与热源直接接触产生燃烧，对木材起支撑作用；（6）石棉网，防止木材离热源面温度过高，减小木材上下层的温差；（7）温度控制仪，测试介质温度，通过介质温度探头来控制电加热源；（8）散热扇，使电机处热量快速散失，防止电机因温度过高造成故障。

图 1 小型木材热处理装置原理图
Fig.1 Schematic diagram of heat-treated equipments

1.3 试验方法

　　本试验的实验方法主要参考芬兰的VVT和木制品工业已经联合开发的工业化规模的炭化木材生产工艺、过热蒸汽法干燥木材标准、高温干燥标准^[2]，进行蒸汽法木材（杉木）热处理工艺的调整，对热处理的参数和升温速度等进行了实验优化。
炭化木的加工主要分为以下三个阶段：第一